Effect of Hydrofluoric Acid Surface Treatments on Surface Roughness and Three-Point Flexural Strength of Suprinity Ceramic
Abstract
Objectives: This study aimed to evaluate the effects of hydrofluoric acid (HF) concentration and etching time on the surface roughness (SR) and three-point flexural strength of Suprinity and to analyze the surface elements before and after etching.
Materials and Methods: To measure the SR, 70 specimens of Suprinity (2×4×5mm3) were assigned to seven groups (n=10). Six groups were etched for 20, 60, and 120 seconds with 5% and 10% HF and 7th group was the control group. Specimens were evaluated using atomic force microscopy (AFM). One specimen from each group was used to analyze the surface elements using scanning electron microscopy (SEM). For measuring the three-point flexural strength, 60 specimens were divided into six groups (n=10) and etched as previously described. The flexural strength was measured using a universal testing machine. T-test, one-way analysis of variance (ANOVA), and two-way ANOVA were used for statistical analyses (P<0.05).
Results: The 10% concentration of HF caused higher SR compared to the 5% HF. The effect of HF concentration on the flexural strength was significantly different in the 20- and 60-second etching groups. Different etching times had no significantly different effect on the SR. With 5% HF, the flexural strength was significantly higher for 20-second etching time than for the etching times of 60 and 120 seconds. With 10% HF, there was a significant difference in flexural strength between etching times of 20 and 120 seconds. The atomic percentage (at%) of silica was enhanced by increasing the etching time.
Conclusions: The best surface etching protocol comprises 10% HF used for 20 seconds.