Effect of Incorporation of Thymol Powder on the Tensile Strength, Elongation Percentage, and Surface Roughness of Room-Temperature Vulcanised Maxillofacial Silicone Material: An In Vitro Study

Abstract

Objectives: Silicone facial prostheses are replaced after a relatively short period of clinical service, mainly due to the decline in their physical and mechanical properties. This study aimed to investigate some mechanical and physical properties of VST-50 maxillofacial silicone after incorporating thymol micro-powder into its matrix.

Materials and Methods: In this in vitro study, room-temperature vulcanised VST-50 maxillofacial silicone and thymol micro-powder were used to prepare the study specimens according to the findings of a pilot study. Sixty specimens were prepared and assigned equally and relevantly to three tests (tensile strength/elongation percentage test, and surface roughness test). Each test encompassed three groups (n=10). According to thymol content percentage, the study groups were customised as: group A: control (without additive), experimental groups B and C with 0.75wt% and 1wt.% thymol additive, respectively. An Instron universal testing machine was used to investigate the tensile strength and elongation percentage, and a profilometer was used to test the surface roughness. ANOVA and post-hoc test were used to analyze the results (alpha 0.05).

Results: Statistically, group B showed a significantly higher mean tensile strength (mean difference: -3.055 N/mm²; P<0.001) and elongation percentage (mean difference: -157.9885%; P=0.003). However, group C showed a significantly lower surface roughness (mean difference: 0.1172µm; P<0.001).

Conclusion: According to the results of this in vitro study, thymol micro-powder appears to be a promising additive that could reinforce some physical and mechanical properties of medical-grade maxillofacial silicone.